These two pressure vessel steel grades P460NH and P355NL2 both owned higher tensile and yield strength. Boiler steel 

plates P460NH tensile strength is at 570_720 Mpa for thickness belows 60mm,even maximum 730 Mpa is OK for the product 

thicknesses up to 16 millimeters.Pressure vessel steel plates P355NL2 tensile strength shall be within 490_630 Mpa for thickness 

belows 60mm,and yield strength shall be above 355Mpa.

 

Steel sheet P355NL2 shall be done low temperature impacting test at minus 50 centi degree on transverse direction at minimum 

27 J energy.Steel sheet P460NH shall be at minus 20 centi degree on transverse at minimum 30 J impacting energy.Now we list 

the mechincal property table of steel P460NH as belows:

 

Mechanical properties for P460NH pressure vessel steel plate:

Yield Strength (Min Mpa)			Tensile Strength ( Mpa)
t≤16	16<t≤40	40<t	t≤60	60<t≤100	100<t
460	445	430	570/720	540/710	-

 

Chemical composition of cast analysis for P460NH boiler steel plate (Max %):

C	Si	Mn	P	S	Al min	N	Cr
0.20	0.60	1.10/1.70	0.025	0.015	0.020	0.025	0.30
Cu	Mo	Nb	Ni	Ti	V	Ni+Ti+V
0.70	0.10	0.05	0.80	0.03	0.20	0.22