High yield strength steel plate and sheet S550QL have to be done Heat treatment under Quenched and tempered.

About the low temperature impacting test,S550QL steel shall be done at minus 40 centi degree.Owned the 

minimum yield strength is above 550 Mpa and the tensile strength shall be within 640_820 Mpa,so S550QL steel 

plates and sheets mainly used in the high strength pressure situiations.

Now our mill equipped with the 4500mm widest roller,and our rolling range for steel plate S550QL shall be the 

thickness from 6mm to 550mm,the width shall be from 1500mm to 4300mm,the length shall be from 5000mm to 

12000mm.Now YUSHENG STEEL indicate the property table for S550QL steel as belows:

 

Mechanical properties for S550QL steel plate:

Yield Strength (Min Mpa)			Tensile Strength ( Mpa)
t≤50	50<t≤100	100<t	t≤50	50<t≤100	100<t
550	530	490	640-820	640-820	590-770

 

Chemical composition of Ladle analysis for S550QL steel plate (Max %):

C	Si	Mn	P	S	N	B	Cr
0.20	0.80	1.70	0.020	0.010	0.015	0.005	1.50
Cu	Mo	Nb	Ni	Ti	V	Zr
0.50	0.70	0.06	2.0	0.05	0.12	0.15