Weathering resistance steel plate S355J0WP under EN10025_5 shall be done impacting test at zero centi degree 

with the minimum energy 27 J.Comparing with steel plate S355J2WP which shall be at _20 centi degree.S355J0WP 

steel has the barrier layer owning to the chemical contents,the formation of this layer can keep approx. four years 

and prevent water,oxygen and sulphur dioxide from contacting the surface of S355J0WP steel plate.Then there is 

no further corrosion for this steel.

 

Generally the delivery condition of S355J0WP shall be under Normalised rolled.

 

Chemical composition of Ladle analysis for S355J0WP steel plate (Max %):

C	Si	Mn	P	S	N	Cr	Cu
0.12	0.75	1.00	0.06-0.15	0.035	0.009	0.30-1.25	0.25-0.55

 

Mechanical properties for S355J0WP steel plate:

Yield Strength (Min Mpa)				Tensile Strength ( Mpa)		Impacting Test
t≤16	16<t≤40	40<t≤100	100<t	t≤100	100<t	℃	J
355	345	-	-	470-630	450-600	0	27